Experimental Study of Leaching and Penetration of Nitrite ions in Nitrite-type Repair Materials on the Surface of Concrete
This study aimed to clarify the leaching properties of nitrite ions in nitrite-type repair materials exposed to rainfall. Repaired concrete specimens were prepared for leaching tests using a lithium nitrite solution, and the amounts of leaching and penetration of nitrite ions were measured under simulated rainfall. The results demonstrated that the amount of leaching could be controlled by using polymer cement paste and mortar surface coatings containing lithium nitrite solution, and by using polymer cement mortar surface coatings following direct lithium nitrite solution coatings. Furthermore, the amount of nitrite ion leaching in all cases was lower than the discharge standard value established by the water pollution control law.
A. M. Rosenberg, et al., “A corrosion inhibitor formulated with calcium nitrite for use in reinforced concrete,” ASTM, STP 629, pp. 89-99, 1977.
A. Kobayashi, S. Ushijima, I. Kamuro, and M. Koshikawa, “A study on the protection of steel in concrete by penetrative corrosion inhibitor,” Journal of Japan Society of Civil Engineers, vol. 1990, no. 420, pp. 51-60, 1990.
T. Hori, S. Yamasaki, and Y. Masuda, “A study on the corrosion inhibiting effect of mortar with high nitrite content,” Concrete Research and Technology, vol. 5, no. 1, pp. 89-98, 1994.
Copyright (c) 2016 Advances in Technology Innovation
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Submission of a manuscript implies: that the work described has not been published before that it is not under consideration for publication elsewhere; that if and when the manuscript is accepted for publication. TAETI is the copyright holder of the journal content on the journal website.
From Jan. 01, 2015, AITI will publish new articles with Creative Commons Attribution Non-Commercial License, under Creative Commons Attribution 4.0 International Public License.
The Creative Commons Attribution Non-Commercial (CC-BY-NC) License permits use, distribution and reproduction in any medium, provided the original work is properly cited and is not used for commercial purposes.